condition	mean	min	max
ATCC 44394, early decay stage, 0-5 mm	2.56652	0.0	5.13304
ATCC 44394, middle late decay stage, 15-20 mm	3.47433	3.3241	3.5638
ATCC 44394, late decay stage, 30-35 mm	4.389386666666667	1.74193	6.56748
SB12	0.7461099999999999	0.0	2.23833
MAD698-R, early decay stage, 0-5 mm	2.2761500000000003	0.0	5.13304
MAD698-R, middle late decay stage, 15-20 mm	3.47434	3.32412	3.5638
MAD698-R, late decay stage, 30-35 mm	4.389396666666666	1.74194	6.56749
MAD698-R	87.43493375	9.18772	451.552
Pure culture	2.77019	1.36496	5.44288
week 6, furfural alcohol (FA10) treated wood	0.0	0.0	0.0
week 6, furfural alcohol (FA40) treated wood	0.0	0.0	0.0
week 6, furfural alcohol (FA70) treated wood	0.0	0.0	0.0
week 9, furfural alcohol (FA40) treated wood	0.3867646153846154	0.0	3.67919
week 3, untreated wood	0.4101641176470588	0.0	6.97279
week 4, untreated wood	0.07361647058823528	0.0	1.25148
week 3, furfural alcohol (FA10) treated wood	0.0	0.0	0.0
week 3, furfural alcohol (FA40) treated wood	0.0	0.0	0.0
week 3, furfural alcohol (FA70) treated wood	0.3212875	0.0	5.1406
week 9, furfural alcohol (FA10) treated wood	2.3799493333333333	0.0	7.5831
week 9, furfural alcohol (FA70) treated wood	0.52236125	0.0	4.55514
week 12, furfural alcohol (FA40) treated wood	0.0	0.0	0.0
week 12, furfural alcohol (FA70) treated wood	0.0	0.0	0.0
week 15, furfural alcohol (FA40) treated wood	0.0	0.0	0.0
week 15, furfural alcohol (FA70) treated wood	0.0	0.0	0.0
week 18, furfural alcohol (FA40) treated wood	0.0	0.0	0.0
week 18, furfural alcohol (FA70) treated wood	0.0	0.0	0.0
week 1, untreated wood	0.0	0.0	0.0
week 2, untreated wood	0.0	0.0	0.0
week 5, untreated wood	0.218339375	0.0	3.49343