condition	mean	min	max
ATCC 44394, early decay stage, 0-5 mm	5.364595	4.59763	6.13156
ATCC 44394, middle late decay stage, 15-20 mm	7.5469566666666665	5.67608	9.92685
ATCC 44394, late decay stage, 30-35 mm	4.68397	2.57952	6.24236
SB12	23.826066666666666	20.4988	27.9872
MAD698-R, early decay stage, 0-5 mm	5.376596666666667	4.59764	6.13157
MAD698-R, middle late decay stage, 15-20 mm	7.546983333333333	5.67609	9.92689
MAD698-R, late decay stage, 30-35 mm	4.68398	2.57952	6.24238
MAD698-R	0.72341375	0.0	2.72033
Pure culture	0.0	0.0	0.0
week 6, furfural alcohol (FA10) treated wood	0.0	0.0	0.0
week 6, furfural alcohol (FA40) treated wood	0.0	0.0	0.0
week 6, furfural alcohol (FA70) treated wood	0.0	0.0	0.0
week 9, furfural alcohol (FA40) treated wood	0.0	0.0	0.0
week 3, untreated wood	0.0	0.0	0.0
week 4, untreated wood	0.0	0.0	0.0
week 3, furfural alcohol (FA10) treated wood	0.0	0.0	0.0
week 3, furfural alcohol (FA40) treated wood	0.0	0.0	0.0
week 3, furfural alcohol (FA70) treated wood	0.0	0.0	0.0
week 9, furfural alcohol (FA10) treated wood	0.0	0.0	0.0
week 9, furfural alcohol (FA70) treated wood	0.0	0.0	0.0
week 12, furfural alcohol (FA40) treated wood	0.0	0.0	0.0
week 12, furfural alcohol (FA70) treated wood	0.0	0.0	0.0
week 15, furfural alcohol (FA40) treated wood	0.0	0.0	0.0
week 15, furfural alcohol (FA70) treated wood	0.0	0.0	0.0
week 18, furfural alcohol (FA40) treated wood	0.0	0.0	0.0
week 18, furfural alcohol (FA70) treated wood	0.0	0.0	0.0
week 1, untreated wood	0.0	0.0	0.0
week 2, untreated wood	0.0	0.0	0.0
week 5, untreated wood	0.0	0.0	0.0