condition	mean	min	max
ATCC 44394, early decay stage, 0-5 mm	10.65085	10.0763	11.2254
ATCC 44394, middle late decay stage, 15-20 mm	2.109373333333333	1.61922	2.61014
ATCC 44394, late decay stage, 30-35 mm	1.2984263333333335	0.683895	2.36357
SB12	0.0	0.0	0.0
MAD698-R, early decay stage, 0-5 mm	9.541246666666666	7.32194	11.2254
MAD698-R, middle late decay stage, 15-20 mm	2.10938	1.61923	2.61015
MAD698-R, late decay stage, 30-35 mm	1.2984276666666668	0.683897	2.36357
MAD698-R	4.38752475	0.624235	8.21633
Pure culture	0.0	0.0	0.0
week 6, furfural alcohol (FA10) treated wood	0.0	0.0	0.0
week 6, furfural alcohol (FA40) treated wood	0.0	0.0	0.0
week 6, furfural alcohol (FA70) treated wood	0.0	0.0	0.0
week 9, furfural alcohol (FA40) treated wood	0.0	0.0	0.0
week 3, untreated wood	0.0	0.0	0.0
week 4, untreated wood	0.0	0.0	0.0
week 3, furfural alcohol (FA10) treated wood	0.0	0.0	0.0
week 3, furfural alcohol (FA40) treated wood	0.0	0.0	0.0
week 3, furfural alcohol (FA70) treated wood	0.0	0.0	0.0
week 9, furfural alcohol (FA10) treated wood	0.0	0.0	0.0
week 9, furfural alcohol (FA70) treated wood	0.0	0.0	0.0
week 12, furfural alcohol (FA40) treated wood	0.0	0.0	0.0
week 12, furfural alcohol (FA70) treated wood	0.0	0.0	0.0
week 15, furfural alcohol (FA40) treated wood	0.0	0.0	0.0
week 15, furfural alcohol (FA70) treated wood	0.0	0.0	0.0
week 18, furfural alcohol (FA40) treated wood	0.0	0.0	0.0
week 18, furfural alcohol (FA70) treated wood	0.0	0.0	0.0
week 1, untreated wood	0.0	0.0	0.0
week 2, untreated wood	0.0	0.0	0.0
week 5, untreated wood	0.0	0.0	0.0